PLAME RESIN
Characteristics and instructions：
Flame retardant resin has the advantages of high oxygen index, high mechanical strength, good water resistance and so on, which is suitable for forming process of hand paste and casting. Products are mainly used in: glass fiber reinforced plastic boat, lifeboat, building materials, cable box and vehicle parts, etc.
|
Item
|
Type
|
Viscosity(25℃ Pa.S)
|
Gel Time (25℃/min)
|
Non-volatile（%）
|
Application & Remarks
|
|
FX-802
|
Additive flame retardant resin
|
|
|
|
With moderate viscosity, thixotropy, good infiltration and good economic performance, it is suitable for medium mechanical strength requirements of flame retardant glass fiber reinforced plastic products.
|
|
FX-107
|
Reactive flame retardant resin
|
0.35-0.65
|
15.0-30.0
|
62-70
|
With high heat distortion temperature, curing speed, penetration resistance. For the production of a high flame retardancy and mechanical strength products.
|
|
FX-3060
|
Reactive flame retardant resin
|
0.15-0.25
|
7.0-15.0
|
60-65
|
For the production of high transmittance, flame retardant, weathering good glass steel products.
|
|
FX-918
|
Reactive flame retardant resin
|
0.30-0.50
|
7.0-15.0
|
60-68
|
Flame retardant marine resin
|
|
FX-918
|
Reactive flame retardant resin
|
0.35-0.60
|
44-82
|
60-68
|
Suitable for all kinds of flame retardant glass fiber reinforced plastic injection process
|
Package and storage:
Net weight:220KG/DRUM. The storage period (below 25℃) is 3 months. Unsaturated polyester resin is a flammable liquid, should be stored at cool and ventilated place, far away from fire and heat source.
Notice:This information is based on the GB standard, since there are many variables in the production process, it is recommended that users need to tested before use. The company reserves the right to modify certain technical parameters.